Tuesday, May 1, 2018

Lacquer - Wikipedia
src: upload.wikimedia.org

The term lacquer is used for a number of hard and potentially shiny finishes applied to materials such as wood. These fall into a number of very different groups.

The term lacquer originates from the Sanskrit word l?ksh? (??????) representing the number 100,000, which was used for both the lac insect (because of their enormous number) and the scarlet resinous secretion, rich in shellac, that it produces that was used as wood finish in ancient India and neighbouring areas.

Asian lacquerware, which may be called "true lacquer", are objects coated with the treated, dyed and dried sap of Toxicodendron vernicifluum or related trees, applied in several coats to a base that is usually wood. This dries to a very hard and smooth surface layer which is durable, waterproof, and attractive to feel and look at. Asian lacquer is sometimes painted with pictures, inlaid with shell and other materials, or carved, as well as dusted with gold and given other further decorative treatments.

In modern techniques, lacquer means a range of clear or coloured wood finishes that dry by solvent evaporation or a curing process that produces a hard, durable finish. The finish can be of any sheen level from ultra matte to high gloss, and it can be further polished as required. It is also used for "lacquer paint", which is a paint that typically dries better on a hard and smooth surface.

In terms of modern products for coating finishes, lac-based finishes are likely to be referred to as shellac, while lacquer often refers to other polymers dissolved in volatile organic compounds (VOCs), such as nitrocellulose, and later acrylic compounds dissolved in lacquer thinner, a mixture of several solvents typically containing butyl acetate and xylene or toluene. Lacquer is more durable than shellac.


Video Lacquer



Etymology

The English lacquer is from the archaic French word lacre "a kind of sealing wax", from Portuguese lacre, itself an unexplained variant of Medieval Latin lacca "resinous substance" from Arabic lakk, from Persian lak, from Hindi lakh (Prakrit lakkha). These ultimately derive from Sanskrit l?ksh? (??????), which was used for both the Lac insect and the scarlet resinous secretion it produces that was used as wood finish. Lac resin was once imported in sizeable quantity into Europe from India along with Eastern woods.


Maps Lacquer



Sheen measurement

Lacquer sheen is a measurement of the shine for a given lacquer. Different manufacturers have their own names and standards for their sheen. The most common names from least shiny to most shiny are: flat, matte, egg shell, satin, semi-gloss, and gloss (high).


Watco 1-qt. Clear Semi-Gloss Lacquer Wood Finish (Case of 6)-63141 ...
src: images.homedepot-static.com


Shellac-based lacquers

In India the insect lac, or Shellac was used since ancient times. Shellac is the secretion of the lac bug (Tachardia lacca Kerr. or Laccifer lacca). It is used for the production of a red dye and pigment (red lake), and for the production of different grades of shellac, used in surface coating.


Watco Clear Lacquer - 63041 - Do it Best
src: doitbest-weblinc.netdna-ssl.com


Urushiol-based lacquers

Urushiol-based lacquers differ from most others, being slow-drying, and set by oxidation and polymerization, rather than by evaporation alone. In order for it to set properly it requires a humid and warm environment. The phenols oxidize and polymerize under the action of an enzyme laccase, yielding a substrate that, upon proper evaporation of its water content, is hard. These lacquers produce very hard, durable finishes that are both beautiful and very resistant to damage by water, acid, alkali or abrasion. The active ingredient of the resin is urushiol, a mixture of various phenols suspended in water, plus a few proteins. The resin is derived from trees indigenous to East Asia, like lacquer tree Toxicodendron vernicifluum, and wax tree Toxicodendron succedaneum. The fresh resin from the T. vernicifluum trees causes urushiol-induced contact dermatitis and great care is required in its use. The Chinese treated the allergic reaction with crushed shellfish, which supposedly prevents lacquer from drying properly. Lacquer skills became very highly developed in Asia, and many highly decorated pieces were produced.

During the Shang Dynasty (1600-1046 BC), the sophisticated techniques used in the lacquer process were first developed and it became a highly artistic craft, although various prehistoric lacquerwares have been unearthed in China dating back to the Neolithic period and objects with lacquer coating in Japan from the late J?mon period. The earliest extant lacquer object, a red wooden bowl, was unearthed at a Hemudu culture (5000-4500 BC) site in China. By the Han Dynasty (206 BC - 220 AD), many centres of lacquer production became firmly established. The knowledge of the Chinese methods of the lacquer process spread from China during the Han, Tang and Song dynasties. Eventually it was introduced to Korea, Japan, Southeast and South Asia.

Trade of lacquer objects travelled through various routes to the Middle East. Known applications of lacquer in China included coffins, music instruments, furniture, and various household items. Lacquer mixed with powdered cinnabar is used to produce the traditional red lacquerware from China.

The trees must be at least ten years old before cutting to bleed the resin. It sets by a process called "aqua-polymerization", absorbing oxygen to set; placing in a humid environment allows it to absorb more oxygen from the evaporation of the water.

Lacquer-yielding trees in Thailand, Vietnam, Burma and Taiwan, called Thitsi, are slightly different; they do not contain urushiol, but similar substances called "laccol" or "thitsiol". The end result is similar but softer than the Chinese or Japanese lacquer. Burmese lacquer sets slower, and is painted by craftsmen's hands without using brushes.

Raw lacquer can be "coloured" by the addition of small amounts of iron oxides, giving red or black depending on the oxide. There is some evidence that its use is even older than 8,000 years from archaeological digs in China. Later, pigments were added to make colours. It is used not only as a finish, but mixed with ground fired and unfired clays applied to a mould with layers of hemp cloth, it can produce objects without need for another core like wood. The process is called "kanshitsu" in Japan. Advanced decorative techniques using additional materials such as gold and silver powders and flakes ("makie") were refined to very high standards in Japan also after having been introduced from China. In the lacquering of the Chinese musical instrument, the guqin, the lacquer is mixed with deer horn powder (or ceramic powder) to give it more strength so it can stand up to the fingering.

There are a number of forms of urushiol. They vary by the length of the R chain, which depends on the species of plant producing the urushiol. Urushiol can also vary in the degree of saturation in the carbon chain. Urushiol can be drawn as follows: R = (CH2)14CH3 or
R = (CH2)7CH=CH(CH2)5CH3 or
R = (CH2)7CH=CHCH2CH=CH(CH2)2CH3 or
R = (CH2)7CH=CHCH2CH=CHCH=CHCH3 or
R = (CH2)7CH=CHCH2CH=CHCH2CH=CH2

Types of lacquer

Types of lacquer vary from place to place but they can be divided into unprocessed and processed categories.

The basic unprocessed lacquer is called raw lacquer (??: ki-urushi in Japanese, shengqi in Chinese). This is directly from the tree itself with some impurities filtered out. Raw lacquer has a water content of around 25% and appears in a light brown colour. This comes in a standard grade made from Chinese lacquer, which is generally used for ground layers by mixing with a powder, and a high quality grade made from Japanese lacquer called kijomi-urushi (????) which is used for the last finishing layers.

The processed form (in which the lacquer is stirred continuously until much of the water content has evaporated) is called guangqi (??) in Chinese but comes under many different Japanese names depending on the variation, for example, kijiro-urushi (????) is standard transparent lacquer sometimes used with pigments and roiro-urushi (????) is the same but pre-mixed with iron hydroxide to produce a black coloured lacquer. Nashiji-urushi (????) is the transparent lacquer but mixed with gamboge to create a yellow-tinged lacquer and is especially used for the sprinkled-gold technique. These lacquers are generally used for the middle layers. Japanese lacquers of this type are generally used for the top layers and are prefixed by the word jo- (?) which means 'top (layer)'.

Processed lacquers can have oil added to them to make them glossy, for example, shuai-urushi (???) is mixed with linseed oil. Other specialist lacquers include ikkake-urushi (??) which is thick and used mainly for applying gold or silver leaf.


Watco 1 gal. Clear Satin Lacquer Wood Finish (Case of 2)-63231 ...
src: images.homedepot-static.com


Nitrocellulose lacquers

Relative to the slow-drying paints and lacquers that preceded them, faster-drying and more durable solvent-based lacquers that contain nitrocellulose, a resin obtained from the nitration of cotton and other cellulosic materials, were developed in the early 1920s, and extensively used in the automobile industry for the next 30 years. Prior to their introduction, mass-produced automotive finishes were limited in colour, damaged easily, and took a long time to dry, with Japan Black being the fastest drying and thus the most economical to use. In 1923, General Motors' Oakland brand automobile was the first to introduce one of the new fast-drying nitrocellulose lacquers, a bright blue, produced by DuPont under their Duco tradename. In 1924 the other GM makes followed suit, and by 1925 nitrocellulose lacquers were thoroughly disrupting the traditional paint business for automobiles, appliances, furniture, musical instruments, caskets, and other products.

Nitrocellulose lacquers are also used to make firework fuses waterproof. The nitrocellulose and other resins and plasticizers are dissolved in the solvent, and each coat of lacquer dissolves some of the previous coat. These lacquers were a huge improvement over earlier automobile and furniture finishes, both in ease of application and in colour retention. The preferred method of applying quick-drying lacquers is by spraying, and the development of nitrocellulose lacquers led to the first extensive use of spray guns. Nitrocellulose lacquers produce a hard yet flexible, durable finish that can be polished to a high sheen. Drawbacks of these lacquers include the hazardous nature of the solvent, which is flammable and toxic, and the hazards of nitrocellulose in the manufacturing process. Lacquer grade of soluble nitrocellulose is closely related to the more highly nitrated form which is used to make explosives. They become relatively non-toxic after approximately a month since, at this point, the lacquer has evaporated most of the solvents used in its production.


Shop Crown 128-fl oz Fast to Dissolve Lacquer Thinner at Lowes.com
src: mobileimages.lowes.com


Acrylic lacquers

Lacquers using acrylic resin, a synthetic polymer, were developed in the 1950s. Acrylic resin is colourless, transparent thermoplastic, obtained by the polymerization of derivatives of acrylic acid. Acrylic is also used in enamel paints, which have the advantage of not needing to be buffed to obtain a shine. Enamels, however, are slow drying. The advantage of acrylic lacquer is its exceptionally fast drying time. The use of lacquers in automobile finishes was discontinued when tougher, more durable, weather- and chemical-resistant two-component polyurethane coatings were developed. The system usually consists of a primer, colour coat and clear topcoat, commonly known as clear coat finishes.


Watco 1 gal. Clear Semi-Gloss Lacquer Wood Finish (Case of 2 ...
src: images.homedepot-static.com


Water-based lacquers

Due to health risks and environmental considerations involved in the use of solvent-based lacquers, much work has gone into the development of water-based lacquers. Such lacquers are considerably less toxic and more environmentally friendly, and in many cases, produce acceptable results. While water-based lacquer's fumes are considerably less hazardous, and it does not have the combustibility issues of solvent based lacquers, the product still dries fairly quickly. Even though its odor is weaker, water-based lacquer can still produce airborne particulates that can get into the lungs, so proper protective wear still needs to be worn. More and more water-based colored lacquers are replacing solvent-based clear and colored lacquers in under hood and interior applications in the automobile and other similar industrial applications. Water based lacquers are used extensively in wood furniture finishing as well.

One drawback of the water based lacquer is that it has a tendency to be highly reactive to other fresh finishes such as quick dry primer (excluding waterborne lacquer primers), caulking and even some paints that have a paint /primer aspect. Tannin bleed-through can also be an issue, depending on the brand of lacquer used. Once it happens, there is no easy fix as the lacquer is so reactive to other products. It is best when planning to spray a white based lacquer over raw wood to source and find a primer that will seal in the tannin. Some painters will use a clear to seal, but several light and fast drying coats must be applied to ensure a good seal. It is then recommended to wait until the next day to start spraying the color so the clear has time to harden and keep the white from pulling the tannin right through the clear. Also, depending on the state / province in which the product is purchased and how familiar the supplier is with wbl, it can be difficult to get any answers from representatives, as many are unfamiliar with the potential reaction problems and how to fix them if they arise.

Water-based lacquer used for wood finishing is also not rated for exterior wear, unless otherwise specified.


Rust-Oleum Automotive 1 gal. Low VOC Professional Lacquer Thinner ...
src: images.homedepot-static.com


Japanning

Just as china is a common name for porcelain, japanning is an old name to describe the European technique to imitate Asian lacquerware. As Asian lacquer work became popular in England, France, the Netherlands, and Spain in the 17th century, the Europeans developed imitation techniques. The European technique, which is used on furniture and other objects, uses finishes that have a resin base similar to shellac. The technique, which became known as japanning, involves applying several coats of varnish which are each heat-dried and polished. In the 18th century, japanning gained a large popular following. Although traditionally a pottery and wood coating, japanning was the popular (mostly black) coating of the accelerating metalware industry. By the twentieth century, the term was freely applied to coatings based on various varnishes and lacquers besides the traditional shellac.




See also

  • Lacquerware
  • Varnish
  • Acetate disc
  • Lacquer painting



References




Further reading

  • Kimes, Beverly R.; Clark, Henry A. (1996), The Standard Catalog of American Cars 1805-1942, Kraus Publications, ISBN 0-87341-428-4  p. 1050
  • Nanetti, Paolo (2006), Coatings from A to Z, Vincentz Verlag, Hannover, ISBN 3-87870-173-X  - A concise compilation of technical terms. Attached is a register of all German terms with their corresponding English terms and vice versa, in order to facilitate its use as a means for technical translation from one language to the other.
  • Webb, Marianne (2000), Lacquer: Technology and Conservation, Butterworth Heinemann, ISBN 0-7506-4412-5  - A Comprehensive Guide to the Technology and Conservation of Asian and European Lacquer
  • Michiko, Suganuma. "Japanese lacquer".